Measured values of relative amplitude permeability μr for a typical conventional grain-oriented electrical steel.
At sufficiently low excitation the material operates in the initial permeability region, in which the permeability is constant and the process is mostly reversible, because the domain walls remain pinned.
The data was measured by S. Zurek.
initial_permeability_cgo_electrical_steel_magnetica.png